Effect of Needle Coke on Gas Permeability of Ceramic Casting Molds

doi:10.1007/s12204-018-2032-8

摘要/Abstract

摘要： The permeability of a new investment casting mold system prepared by adding needle cokes has been investigated in this work. The permeability tests of the molds were carried out at the temperature of 25—1 200 ?C. The results showed that the addition of needle cork could significally increase the permeability of the molds by a factor of about 4 because the burning of needle cokes increased the porosities of the molds. Meanwhile, the needle coke modified molds exhibited higher green strength and greater thickness both on flat section and at sharp edges compared with the full fused silica mold. Taking account of the mold thickness, the needle coke modified molds had increased adjusted fracture load (AFL) by a factor of about 2 at the test temperature of 25—1 200 ?C. The addition of needle coke significally improved the permeability of the molds during both autoclaving and casting, and optimized the correlation between the permeability and green strength of the molds.

关键词: permeability, mold, needle coke, strength, investment casting

Abstract: The permeability of a new investment casting mold system prepared by adding needle cokes has been investigated in this work. The permeability tests of the molds were carried out at the temperature of 25—1 200 ?C. The results showed that the addition of needle cork could significally increase the permeability of the molds by a factor of about 4 because the burning of needle cokes increased the porosities of the molds. Meanwhile, the needle coke modified molds exhibited higher green strength and greater thickness both on flat section and at sharp edges compared with the full fused silica mold. Taking account of the mold thickness, the needle coke modified molds had increased adjusted fracture load (AFL) by a factor of about 2 at the test temperature of 25—1 200 ?C. The addition of needle coke significally improved the permeability of the molds during both autoclaving and casting, and optimized the correlation between the permeability and green strength of the molds.

中图分类号:

TB 321

WANG Fei (王飞), ZHU Guoliang (祝国梁), LI Fei (李飞), SUN Baode (孙宝德). Effect of Needle Coke on Gas Permeability of Ceramic Casting Molds[J]. Journal of Shanghai Jiao Tong University (Science), 2018, 23(Sup. 1): 124-131.

参考文献 20

[1]	PATTNAIK S, KARUNAKAR D B, JHA P K. Developmentsin investment casting process: A review[J]. Journal of Materials Processing Technology, 2012,212(11): 2332-2348.
[2]	SARIDIKMEN H, KUSKONMAZ N. Properties ofceramic casting molds produced with two differentbinders [J]. Ceramic International, 2005, 31(6): 873-878.
[3]	MUELLER H J. Particle and pore size distributions ofinvestments [J]. Journal of Oral Rehabilitation, 1986,13(4): 383-393.
[4]	REZA F, TAKAHASHI H, IWASAKI N, et al. Effectsof investment type and casting system on permeabilityand castability of CP titanium [J]. The Journal ofProsthetic Dentistry, 2010, 104(2): 114-121.
[5]	SYVERUD M, HERO H. Mold filling of Ti castingsusing investments with different gas permeability [J].Dental Materials, 1995, 11(1): 14-18.
[6]	MATYSIAK H, HARATYM R, KLABCZYK M. Gasflow through a multilayer ceramic mould in lost waxfoundry process [J]. Archievs of Foundry Engineering,2009, 9(2): 155-158.
[7]	YUAN C, JONES S, BLACKBURN S. Developmentof a new ferrous aluminosilicate refractory material forinvestment casting of aluminum alloys [J]. Metallurgicaland Materials Transactions A, 2012, 43(13): 5232-5242.
[8]	YUAN C, JONES S. Investigation of fibre modifiedceramic moulds for investment casting [J]. Journal ofthe European Ceramic Society, 2003, 23(3): 399-407.
[9]	JONES S, YUAN C. Advances in shell moulding forinvestment casting [J]. Journal of Materials ProcessingTechnology, 2003, 135(2/3): 258-265.
[10]	DOLES R S, VIERS D S. Filler component for investmentcasting slurries: US20070931330 [P]. 2008-02-28[2018-11-06].
[11]	LU K, LIU X D, DU Z X, et al. Properties of hybridfibre reinforced shell for investment casting [J]. CeramicsInternational, 2016, 42(14): 15397-15404.
[12]	KLINE D M, LEKAKH S N, RICHARDS V L. Improvinginvestment casting mold permeability usinggraphite particles [J]. Transactions of the AmericanFoundry Society, 2010, 118: 159-165.
[13]	YUAN C, JONES S, BLACKBURN S. The influenceof autoclave steam on polymer and organic fibre modifiedceramic shells [J]. Journal of the European CeramicSociety, 2005, 25(7): 1081-1087.
[14]	KLINE D M. Controlling strength and permeability ofsilica investment casting molds [D]. Rolla, MO, USA:Missouri University of Science and Technology, 2010.
[15]	PARK C W, YOON S H, OH S M. An EVS (electrochemicalvoltage spectroscopy) study for the comparisonof graphitization behaviors of two petroleumneedle cokes [J]. Carbon, 2000, 38(9): 1261-1269.
[16]	WANG F, LI F, HE B, et al. Microstructure andstrength of needle coke modified ceramic casting molds[J]. Ceramics International, 2014, 40(1): 479-486.
[17]	Investment Casting Institute. Ceramics testing guidebook[M]. New Jersey: Investment Casting Institute,1989.
[18]	JONES S, JOLLY M R, LEWIS K. Development oftechniques for predicting ceramic shell properties forinvestment casting [J]. British Ceramic Transactions,2002, 101(3): 106-113.
[19]	KOPONEN A, KATAJA M, TIMONEN J. Permeabilityand effective porosity of porous media [J]. PhysicalReview E, 1997, 56(3): 3319-3325.
[20]	KOPONEN A, KATAJA M, TIMONEN J. Tortuousflow in porous media [J]. Physical Review E, 1996,54(1): 406-410.